Crystallization of Nd<sub>2</sub>Fe<sub>17</sub>B<sub>x</sub> from its stoichiometric melt composition

Gao, J. R. und Volkmann, T. und Yang, S. und Reutzel, S. und Herlach, D. M. und Song, X. P. (2007) Crystallization of Nd<sub>2</sub>Fe<sub>17</sub>B<sub>x</sub> from its stoichiometric melt composition. Journal of Alloys and Compounds, 433, Seiten 356-362. Elsevier. DOI: 10.1016/j.jallcom.2006.06.090.

[img]
Vorschau
PDF - Requires a PDF viewer such as GSview, Xpdf or Adobe Acrobat Reader
711kB

Kurzfassung

Containerless solidification of gas-atomized Nd<sub>10</sub>Fe<sub>85</sub>B<sub>5</sub> melt droplets was carried out using the drop tube technique. The phase constituents and microstructure of the solidified samples were investigated by means of powder X-ray diffraction analysis, thermomagnetic analysis, and scanning electron microscopy. Besides <font face="symbol">g</font>-Fe and Nd<sub>2</sub>Fe<sub>14</sub>B, non-equilibrium phases such as Nd<sub>2</sub>Fe<sub>17</sub>B<sub>x</sub>, <font face="symbol">e</font>-Nd, and Nd<sub>1.1</sub>Fe<sub>4</sub>B<sub>4</sub> were identified. The microstructure of the samples was categorized into three types, including a quasi-single phase one that consists mainly of Nd<sub>2</sub>Fe<sub>17</sub>B<sub>x</sub> dendrites. The lattice parameters and Curie temperature of Nd<sub>2</sub>Fe<sub>17</sub>B<sub>x</sub> were determined, and compared with those of the same type phase crystallized in Nd-rich Nd-Fe-B melt compositions. The results were discussed with respect to the stoichiometry, formation as well as potential applications of Nd<sub>2</sub>Fe<sub>17</sub>B<sub>x</sub>.

Dokumentart:Zeitschriftenbeitrag
Titel:Crystallization of Nd<sub>2</sub>Fe<sub>17</sub>B<sub>x</sub> from its stoichiometric melt composition
Autoren:
AutorenInstitution oder E-Mail-Adresse der Autoren
Gao, J. R.Northeastern University, Shenyang, China
Volkmann, T.NICHT SPEZIFIZIERT
Yang, S.Xi'an Jiaotong University, Xi'an, China
Reutzel, S.Ruhr-Universität Bochum
Herlach, D. M.NICHT SPEZIFIZIERT
Song, X. P.Xi'an Jiaotong University, Xi'an, China
Datum:2007
Erschienen in:Journal of Alloys and Compounds
Band:433
DOI :10.1016/j.jallcom.2006.06.090
Seitenbereich:Seiten 356-362
Verlag:Elsevier
Status:veröffentlicht
Stichwörter:Unterkühlung von Materialien
HGF - Forschungsbereich:Verkehr und Weltraum (alt)
HGF - Programm:Weltraum (alt)
HGF - Programmthema:W FR - Forschung unter Weltraumbedingungen (alt)
DLR - Schwerpunkt:Weltraum
DLR - Forschungsgebiet:W FR - Forschung unter Weltraumbedingungen
DLR - Teilgebiet (Projekt, Vorhaben):W - Vorhaben Materialforschung unter Mikro-g (alt)
Standort: Köln-Porz
Institute & Einrichtungen:Institut für Materialphysik im Weltraum > Institut für Raumsimulation > Zentrum für die Erstarrung unterkühlter Schmelzen (ZEUS)
Hinterlegt von: Dr.rer.nat. Sven Reutzel
Hinterlegt am:08 Jan 2008
Letzte Änderung:12 Dez 2013 20:20

Nur für Mitarbeiter des Archivs: Kontrollseite des Eintrags

Blättern
Suchen
Hilfe & Kontakt
Informationen
electronic library verwendet EPrints 3.3.12
Copyright © 2008-2013 Deutsches Zentrum für Luft- und Raumfahrt (DLR). Alle Rechte vorbehalten.